HY 4070 Hybrid Gel Adhesives, 10 mL Cartridge, Clear, 10/Case

Two-part, transparent, cloudy colorless to pale yellow cyanoacrylate/acrylic hybrid gel adhesive
Provides a fast fixture at room temperature
It suits various substrates including most plastics, rubbers and metals
Used where complete cure of excess adhesive, as well as temperature and moisture resistance, is required
Non-sag
Gel consistency prevents adhesive flow, even on vertical surfaces
Curing is initiated on mixing the Part A and Part B components
Handling strength is achieved rapidly
Full strength is achieved over time

Quantity 10EA/CA

Specifications

Adhesive Tensile Shear=0.1 N/mm²
Applicable Materials=Metal; Plastic; Rubber
Application Temp. Range [Max]=+25 C
Applications=Bonding
Capacity Vol. [Nom]=10 mL
Chemical Compound=Ethyl 2-Cyanoacrylate; Methacrylate
Color=Clear
Elongation [Nom]=4.9 %
Fix Cure Time @ Temp.=4 min to 6 min (2 mm Gap) @ +25 C; <60 s (0.05 mm Gap) @ +25 C
Fixture Time=4 min to 6 min (2 mm Gap); <60 s (0.05 mm Gap)
Flash Point [Nom]=+176 F to +199.4 F (Part A); +230 F (Part B)
Gap Fill [Nom]=0.05 mm
Hardness [Nom]=65 Shore D
Language=English
Packing Type=Cartridge
Physical Form=Gel
Ratio=10:1
Resistance=Moisture; Temperature
Specific Gravity [Nom]=1.05 to 1.1
Temp. Range [Max]=+25 C
Tensile Strength [Nom]=2117 psi
Type=Hybrid Gel Adhesive
Usage=Bonding
VOC=< 3 %
Viscosity [Max]=1300 mPa (Part A); 30 mPa (Part B)
Viscosity [Min]=1 mPa (Part B); 200 mPa (Part A)
Viscosity [Nom]=1 to 30 mPa (Part B); 200 mPa to 1300 mPa (Part A)
Working Time [Max]=4 min
Working Time [Min]=1 min
Working Time [Nom]=1 min to 4 min
Wt.=11 g